HYDROSAFE®
Fire protection casting and filling compound
- general construction supervision test report
Nr. P-3943/8797
- construction material class A1 according to DIN 4102-1 part 1
Provisions of the state construction laws:
When installing components in terms of fire safety regulations into walls and ceilings, the resulting gaps are to be filled with non-flammable materials of construction material class A1.
Preliminaries - processing time:
Hydrosafe fire protection casting compound is to be mixed with the required amount of water. Immediately after, the encapsuling can be started. When mixed, the compound will remain fluid up to one hour. Additional compressing after spreading the compound is not necessary either.
Special features:
In the case of fire, HYDROSAFE fire protection casting compound offers a high level of efficiency. The substances anhydrite and alpha hemihydrate contained in the casting compound are almost completely converted into calcium sulfate dihydrate by the added water. During this process, almost 95% of the water is converted into crystalline water. The crystalline water will be re-liquified at about 140° C and will be released. This process will absorb great amounts of energy in the case of fire
Bundle options:
HYDROSAFE fire protection casting and filling compound is available in several bundle options:
| | Packaging | filling volume |
|---|
| Casting compound |
bag |
20 kg |
| Casting & filling compound |
bucket |
10 kg |
| Casting & filling compound |
bucket |
5 kg |
If you are planning on purchasing a large volume, you may want to consider the following packaging units.
| | bundle option | quantity/pallet |
|---|
| Casting compound |
bag à 20 kkg |
50 bags |
| Casting & filling compound |
bucket à 10 kg |
32 buckets |
| Casting & filling compound |
bucket à 5 kg |
56 buckets |
Productvideo
Practical application
Practical application
HYDROSAFE fire protection casting and filling compound does not need to be used with special tools. It is able to reach and fill the smallest of gaps.
HYDROSAFE fire protection casting compound
Due to its ease of application, HYDROSAFE fire protection casting compound is especially well suited for the filling of thermo units, fire dampers, door and window frames, ceiling breakthroughs, pipe and channel openings, mounting frames of all kinds and separator plates
HYDROSAFE fire protection filling compound
Due to its ease of application, HYDROSAFE fire protection filling compound is especially well suited for filling and sealing gaps and tears against fire and smoke. Of course, our filling compound can also be used for the filling of thermo units, fire dampers, door and window frames, ceiling breakthroughs, pipe and channel openings, mounting frames of all kinds and separator plates.
Instructions for use:
HYDROSAFE fire protection casting and filling compound shall be mixed with water until smooth using a stirrer or a whisk.
| HYDROSAFE dried goods/kg | water/l | usable mass/l |
|---|
| 20 kg |
4,4 l |
12 l |
| 10 kg |
2 l |
6 l |
| 5 kg |
1 l |
3 l |
Technology
Technology
| | HYDROSAFE fire protection casting compound | HYDROSAFE fire protection filling compound |
|---|
| colour |
light grey |
light grey |
| consistency |
powder |
powder |
| bulk weight |
0,8 kg/dm3 |
1,92 kg/dm3 |
| dry bulk density |
1,96 kg/dm3 |
|
| yield |
0,6 l/kg |
0,6 l/kg |
| processing temperature |
+ 5 °C bis + 35 °C |
+ 5 °C bis 35 °C |
| processing time |
ca. 60 min |
ca. 30 min |
| shrinkage / flow spread |
25 cm (Vicard-Ring) |
0,25 mm/lfd m min |
| fresh matter density |
2,1 kg/dm³ |
2,1 kg/dm³ |
| air void content |
> 10 % |
> 10 % |
| water absorption when dry |
2,13 %/24 h |
2,13 %/24h |
| drying time (coating thickness) |
1 Tag/mm |
1 Tag/mm |
| setting time (until resilient) |
6 h |
12 h |
| cleaning |
using water (mechanical) |
using water (mechanical) |
| Lastorage |
dry on (wooden) pallet |
dry on (wooden) pallet |
| storage life |
6 months |
6 months |
| storage temperature |
not > 35 °C |
not > 35 °C |